6082 aluminum plate profile processing process will encounter a lot of problems, sometimes we found scratch, if you can not find out the problem, then there is no way to avoid scratch, the 6082 aluminum plate manufacturer will give you a brief introduction, 6082 aluminum plate profile processing process appears the reason for scratch.

1, double holes or porous mould of 6082 aluminum extrusion profiles, because the rate is not well at the time of the die hole, profiles and not neat, the length of the high temperature entrances that happened scratch each other's 6082 aluminum profiles, cause not smooth surface, air oxidation angled bruises after dark black, it is 6082 aluminum profile products processing enterprises in the waste material extrusion molding.

2, 6082 aluminum plate profile processing mold use too long, mold blank cutter, support pad, special pad and other exit with a lot of aluminum metal material, profile flow diameter mold empty knife, support pad, special pad, so that the profile scratches.This seems to be a very small case.

3, the cold bed side of the 6082 aluminum plate using profiles, sometimes in the iron shelf is not neat, may lead to the 6082 aluminum profile with tooth scratches, especially all kinds of profiles for planar and wider profiles or bending or arc profiles directly lead to the enterprise surface abrasion probability influence is greater!

Aluminum alloy profile processing finished saw table, storage rack, frame profile, sorting congestion saw, which lift extract, very easy to lead to mutual wear, whether there will be water chestnut leads to the demarcation of the profile.

5. 6082 aluminum profile shakes and swings too much in the whole process, and the lining fixation is not good.

The above is about 6082 aluminum plate profile processing in the cause of abrasion, we can refer to the above reasons for analysis and find out the solution, if you need 6082 aluminum plate can contact us.