We all know that 6063 aluminum plate needs to be processed by heat treatment. The common state of 6063 aluminum plate is T6 state, and in fact there are T4 and T5 states. Next, 6063 aluminum plate manufacturer will tell you the specific introduction of different states of 6063 aluminum plate.

The 6063 aluminum is extruded by the extruder after the cooling process of T4 aluminum, but it does not enter the aging oven.Without aging treatment, low hardness, easy to process, suitable for late bending deformation processing.

The 6063 aluminum plate T5 is quenched by air cooling control after extrusion, and then kept for about 2-3 hours in a rotary aging furnace with a temperature of 200 degrees.The aluminum profile can be T5.Aluminum after discharge is relatively high in hardness and has a certain degree of deformability, which is widely used in the construction industry.

The tempered aluminum 6063 T6 is quenched by water, and the aging temperature will be higher after artificial quenching, and will be maintained for a longer time to achieve a higher state of hardness.The 6063-T6 aluminum plate is suitable for the industry with high hardness.

The specific introduction of different states of 6063 aluminum plate is over here. If you need 6063 aluminum plate, please consult us.