In general, the mechanical properties of 6063 aluminum plate in the use of the national standards, we 6063 aluminum plate manufacturers in the production need to pay attention to some of the factors affecting the mechanical properties of 6063 aluminum plate, the following will give you a specific analysis.

1. Chemical composition of aluminum alloy ingots

6063 aluminum plate should first determine the content of strengthening phase, its tensile strength, the increase of the increased amount of Mg2Si approximate linear deformation resistance but also follow, processing difficult, but when Mg2Si amount is less than 0.72%, for small coefficient of extrusion products, tensile strength values are in danger of short of standard requirement, when Mg2Si quantity more than 0.9%, alloy plastic has a downward trend.The content of magnesium should be determined after determining the number of strengthening phases.Magnesium is a flammable metal.In determining the control range of magnesium, the error caused by burning should be considered, but should not be too large, so as not to lose control of the properties of the alloy.

2. Homogenization of aluminum alloy ingots

The homogenization treatment can improve the plasticity of the ingots, improve the technical performance, improve the heteromorphism of the domestic products enterprises, and eliminate the residual stress in these metal companies.

3. Extrusion temperature and speed of 6063 aluminum plate

The quenching temperature of 6063 aluminum plate shall not be less than 500 degrees, so the extrusion temperature is generally controlled at 470-- 490 degrees. The specific extrusion temperature and extrusion speed shall be adjusted appropriately according to the wall thickness of the profile, extrusion characteristics and mold condition, and the extrusion principle of high temperature, low speed, low temperature and high speed shall be adhered to.

4. Quenching effect of 6063 aluminum plate

Quenching is to metal at high temperature solid soluble in matrix of Mg2Si after the mold was retained by the rapid cooling to room temperature, and cooling rate and strengthening phase is proportional to the content, often because of its higher quenching sensitivity, for 0.8% of the 6063 aluminum plate, in Mg2Si cool from 454 degrees to 204 degrees of critical cooling temperature range, small cooling speed is 38 degrees per minute, as a result, 6063 aluminum plate can use air cooling quenching, even good quenching effect can effectively improve the product mechanical properties.

The above is the introduction of the factors affecting the mechanical properties of 6063 aluminum plate. If you need to consult the price of 6063 aluminum plate, please contact us.