Aging furnace is a necessary equipment in the production of 6061 aluminum plate. What is the effect of aging furnace on the production of 6061 aluminum plate?Next 6061 aluminum plate manufacturers to give you a specific introduction.

Effect of aging temperature:

The critical nucleus size and amount of precipitates are different for ovens aging at different temperatures.If the temperature is too low, the diffusion will be very slow, after the aging of hard over low, the strength is certainly not up to;If the aging temperature is too high, the diffusion rate is accelerated, and the critical crystal nucleus of the precipitated phase is too large, the hardness will not be enough to reach the strength we need. Only when the aging temperature of 6061 aluminum plate is fixed, can the produced 6061 aluminum plate really reach a corresponding strength.

How long should it be kept from quenching to artificial aging:

After quenching, 6061 aluminum plate is placed for a period of time before artificial aging, the strength of 6061 aluminum plate will decrease somewhat, but the plasticity will increase.Artificial aging one day after quenching may have some influence on the strength, so the length of time from quenching to artificial aging determines the strength and plasticity of 6061 aluminum plates.

Again, the chemical composition of aluminum alloy:

Whether the alloy design elements of 6061 aluminum plate can be dissolved in the solid solution and how big the solid solution can be with the change of temperature determine whether 6061 aluminum plate can be treated with different aging problems.Some binary alloys, ternary alloys and multiple alloys can be used to strengthen the heat treatment, the specific aluminum alloy into the composition, because the solubility of different aluminum alloy composition and solid phase transition are different.

Solid solution treatment of alloy:

It is also very important to master the solution treatment process of 6061 aluminum plate.As long as the quenching temperature is increased and the heat preservation time is prolonged, the solid solution can be kept even and full, and good aging strengthening effect can be obtained for 6061 aluminum plates.It is important to note that if the nucleus ACTS, the second-stage precipitation may cause uneven precipitation phenomenon, which does not obtain the good aging hardening effect of the mass 6061 aluminum produced by quenching the poor.

What effect the aging furnace has on the production of 6061 aluminum plate is introduced here, if you need 6061 aluminum plate, you can consult us.