After the 6063 aluminum tube is discharged from the die hole, the contact with tools, equipment and other tools in the subsequent process may lead to surface damage, scratches, scratches. Then the 6063 aluminum tube manufacturer will give you an analysis of the main reasons and solutions.

The main causes of 6063 aluminum tube scratches, bruises and bruises

1. The surface of 6063 aluminum tube ingot can be attached with debris or ingot composition segregation.There are hard metal particles in the cast ingot of the 6063 aluminum tube. During the extrusion process, these metal particles attach to the surface of the working belt or cause serious damage to the working belt, and eventually scratch the surface of the 6063 aluminum tube.

2. There are bare metal or hard inclusions on the discharging track or the laying bed. When it comes into contact with the 6063 aluminum tube, the surface of the 6063 aluminum tube will be seriously scratched;

3. When the 6063 aluminum tube profile can be delivered from the discharge track to the swing bed by the fork lever, the development speed increases too fast, which may easily lead to the collision of different profiles;

4. Scratches caused by the tug on the bed;

5. Causing serious damage during transportation.

The solution of 6063 aluminum tube scratches, abrasions and bruises

1. Strengthen the control of ingot quality;

2, improve the quality of mold repair, regular nitriding, strict implementation of nitriding technology;

3. Use a soft cushion between the 6063 aluminum tube and the auxiliaries to minimize the contact oxidation damage between the 6063 aluminum tube and the auxiliaries;

4, 6063 aluminum tube production should be handled lightly, do not drag or flanged profiles;

5. Place the 6063 aluminum tube reasonably in the feed frame to avoid mutual friction as far as possible.

The main causes and solutions of 6063 aluminum tube scratches, scrapes and bruises are introduced here. If you need to know the price of 6063 aluminum tube, you can consult us.