6063 aluminum plate is often used in building materials, such as doors and Windows and curtain walls, etc., it is generally needed to anodize 6063 aluminum plate before use, then sometimes there will be uneven oxide film, the cause of this phenomenon is what?Is there a solution?Next 6063 aluminum plate manufacturers to detail.

1. First of all, it is possible that the vibration range in the tank is too large, which will lead to different colors of the oxide film.

The solution is to control the speed of the oxidant, the fluctuation should be small, and the operation should be smooth.In addition, the temperature of the solution should not be too low, otherwise you will see the spots on the surface of the 6063 aluminum plate.

2, followed by 6063 aluminum plate surface damage, wear, oxidation will cause uneven color.

The solution is to put the good quality, control the material problem of 6063 aluminum plate, to ensure that no damage.

3, there are: the problem of the operation process, such as alkali corrosion treatment is not thorough enough, can not remove the oxide film and dirt on the original parts of 6063 aluminum plate;After alkaline corrosion, the surface is still alkaline. The workpiece of 6063 aluminum plate has improper contact with foreign bodies in the process of transfer.

The solution is to clean the surface of 6063 aluminum plate before deep processing, and reduce unnecessary friction in the process of transportation.

The above is about the causes and solutions of the color imbalance of 6063 aluminum plate oxide film, want to know the price of 6063 aluminum plate, you can contact us.