We all know that aluminum alloy material will have better performance after oxidation, so what should we pay attention to after oxidation of 2A12 aluminum plate?Next 2A12 aluminum plate manufacturers to give you a detailed introduction.

1. Hot water can be used to rinse the film for aging.However, the temperature and time of the water must be strictly controlled, the temperature of the film, the color of the light too high thinning.The appropriate temperature and time is: temperature 40 ~ 50℃ time 0.5 ~ 1MIN.

2. It is better to dry by natural air. The workpiece washed by hot water is hung on the shelf, so that the water on the surface of 2A12 aluminum plate flows downwards, and then the film color can be absorbed by towel.

3. Aging, which can be determined according to the climatic conditions, can be exposed to sunlight in summer, and can be baked in oven in rainy days or winter. The technological conditions are as follows: temperature 40~50℃ time 10 ~ 15

4. Repair of defective units.The component should be dried with defective conductive oxide film, which should be picked out before the aging step. Through drying, aging of the film after peeling is difficult and will affect the surface roughness of the aluminum plate 2A12.First, we clamp the unqualified workpiece to the fixture, and then conduct an anodic treatment for 2 ~ 3min. After the film layer is soft and falls off, it can be re-designed and analyzed for conductive anodization after a little cleaning of alkali liquid and the light of nitric acid.

Please refer to the situation that needs to be paid attention to after oxidation of 2A12 aluminum plate. If you need 2A12 aluminum plate, please consult us.